Prod Model: |
BHLJ-S-C-Y104 |
Country Of Origin: |
Beihai, Guangxi, China |
Oxidation Reaction: |
Hc + O2 = H2O + CO2 |
Reduction Reaction: |
Nox + Hc + Co = N2 + H2O + CO2 |
Scope: |
Suitable for Gas Fuel Engines |
Function: |
Engine Exhaust Gas Purification |
Usage: |
Special Equipment |
Processing Methods: |
Physics and Chemistry |
Pullution Sources: |
Air Pollution Control |
Air Pollution Control Equipment Type: |
Gaseous Pollution Purification Equipment |
Structure: |
Equipment |
Discharge Standard: |
Euro IV |
Certification: |
TS16949 |
Component: |
Catalytic Converter |
Main Market: |
World Wide |
Body Material: |
Ceramic |
Product Description
Brand | GXLJ |
Product | HONDA ACCORD 1995 1996 1997 1998 1999 2000 2001 2002 Catalytic Converter |
Material | Cordierite, mullite, corundum-mullite |
Advantage | 1. Thin wall of hole 2. Large surface area 3. Back pressure small 4. High compressive strength 5. Small thermal expansion coefficient 6. High temperature resistance(melting point 1400degree) 7. Good Heat resistant to impact ,seismic performance 8. Have a good match and all sorts of catalyst active component 9. Good Cold start performance,Low light-off temperature, fast temperature elevation,Small resistance of gas,high conversion rate |
Application | Used for engine exhaust gas purification system of ceramic catalyst carrier/support. The carrier surface coated with a catalyst, in the automobile exhaust through, will be harmful ingredients such as HC, CO, NOX in the exhaust into harmless ingredients. Eliminate organic exhaust gas and odour |
Pore density | 25-600CPSI |
Pore shapes | Circular, rectangular and triangle |
Sectional shape | Circular, square, rectangular, oval, lane-shape and special-shape |
Emission Standard | Euro III, Euro IV, Euro V. |
Delivery terms | FOB, CIF, CFR, DDP, EXW |
Payment terms | By T/T, 100% after sign the contract or 40% down payment before production, 60% balance before delivery. |
Delivery time | Within 30-45 days after receiver payment. |
Packing | Corrugated carton, wooden box, pallet, as per customer's request. |
Different formulas for your selection, it's economics of emissions compliance products.
More details and further information, pls chk it out with us.
Property of Cordierite honeycomb ceramic
Material | Cordierite |
Structure property | Cell type | -- | Square |
Number of cell | Cell/in2 | 100 | 200 | 300 | 400 |
Cell distance | mm | 2.54 | 1.75 | 1.47 | 1.27 |
Thickness of wall | mm | 0.43 | 0.32 | 0.25 | 0.17 |
Hole fraction | % | 63 | 68 | 63 | 71 |
Porous density | g/cm3 | 0.71 | 0.55 | 0.60 | 0.43 |
Geometric surface area | mm2/mm3 | 13.0 | 18.9 | 21.7 | 26.8 |
Physics property | True density | -- | 2.0 |
Water absorption | Normal | wt% | 20~24 |
Boiling | wt% | 27~35 |
Coefficient of thermal expansion(40~800ºC) | X10-6/ºC | <1.5 |
Softening temperature | ºC | ≥1380 |
Compressive strength | Mpa | >9.9 |
Runway Model ( oval ) | φ169*85.7*127 | Round | φ150*100 |
φ148*84*127 | φ150*75 |
φ144.8*81*76.2 | φ125*130 |
φ144.8*81.3*75 | φ144*152 |
φ127*63.5*127 | φ118*152 |
φ145*80*80 | φ106*150 |
φ93*61*90 | φ106*100 |
φ120.6*80*65 | φ103*100 |
φ120*80*75 | φ101.6*100 |
φ147*96*75 | φ100*100 |
φ100*100*75 | φ93*130 |
φ50*50*25 | φ125*100 |
Ellipse broad 80*long φ153*100 | φ125*130 |
General specification:
Project | Index |
CFT-02(260 holes) | CFT-03(300 holes) | CFT-04(400holes) | CFT-06(600 holes) |
Density KG/dm(g/cm³) | ≤0.70 |
Water absorption% | 20-27 |
Temperature compressive strength KN/cm² | X direction ( the direction perpendicular to the line X in channel ) | ≥50 | ≥50 | ≥65 |
Y direction ( perpendicular to the line direction Y of the bore ) | ≥160 | ≥180 | ≥200 |
Coefficient of thermal expansion ( line ) (20-800ºC) | ≤1.50*10^6 |
0.1Mpa RUL ºC | >1450 |
Air-cooled thermal stability of 800 ºC | ≥3 |
The apparent surface area cm²/cm³ | ≥20 |
Chemical composition range (%) | AI2O3 | SiO2 | MgO | K.Na2O | Fe2O2 | other |
31-34 | 48-51 | 12-14 | <1 | <0.5 | <1 |
Specific heat 20-100ºC J/KG.K | 800-900 | 800-950 | 800-1200 | 750-800 | 850-1100 | 840-920 |
Thermal conductivity 20-100ºC W/m.k | 1.5-2.5 | 1.4-2.0 | 1.5-2.5 | 1.5-1.5 | 1.5-2.3 | 1.0-1.2 |